304L Stainless Steel Tube ASME SA213 TP304L ASTM A213 TP304L
ASTM A269 304L Stainless Steel Tubing, ASTM A213 SA213 TP304L Stainless Steel Tube, ASTM A312 SA312 TP 316L Stainless Steel Pipe, Stainless Steel 304L Pipes, ASTM A213 SA213 304L U bend Tubes, EN 10216-5 1.4307 Stainless Steel Tubes in China. ASTM A312 SA312 TP 316L Stainless Steel Pipe, Stainless Steel 304L Pipes, ASTM A213 SA213 304L U bend Tubes, EN 10216-5 1.4307 Stainless Steel Tubes in China. Stainless Steel 304L Pipes.
Outside Diameter: 6 – 530mm
Wall Thickness: 0.50 – 64mm
Standard Specification:
EN 10216-5; DIN 17456, DIN 17458, DIN 2462, DIN 17455
GB/T14975; T14976; T13296; GB5310;
ASTM A213, A269, A312, A511, A789, A790, A928, A999, A1016, ASTM B161, ASTM B163, ASTM B165, ASTM B167, ASTM B338, ASTM B407, ASTM B423, ASTM B444,ASTM B619, ASTM B622, ASTM B626, ASTM B668, ASTM B677, ASTM B829
JIS G3459, JIS G3463, JIS G3446, JIS G3447, JIS G3448, JIS G3468
GOST 9940;GOST 9941;
Chemical Composition:
| Grade | – | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| 304L/S30403 | min.max. | -0.035 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-12.0 | – |
| 304/S30400 | min.max. | -0.08 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4301 | min.max. | -0.07 | -2 | -1 | -0.04 | -0.015 | 17.00-19.5 | – | 8.0-10.5 | -0.11 |
| EN 10216-5 1.4307 | min.max. | -0.03 | -2 | -1 | -0.04 | -0.015 | 17.5-19.5 | – | 8.0-10.0 | -0.11 |
| 304H /S30409 | min.max. | 0.04-0.10 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | – | 8.0-11.0 | – |
| EN 10216-5 1.4948 | min.max. | 0.04-0.08 | -2 | -1 | -0.035 | -0.015 | 17.0-19.0 | – | 8.0-11.0 | -0.11 |
Mechanical Properties:
| – | Tensile Strength | Yield Strength | Elongation | Hardness | Hardness |
| Grade | (MPa) min | 0.2% Proof (MPa) min | (% in 50mm) min | Rockwell B (HR B) max | Brinell (HB) max |
| 304L | 485 | 170 | 35 | 90 | 192 |
| 304 | 515 | 205 | 35 | 90 | 192 |
| 304H | 515 | 205 | 35 | 90 | 192 |
Physical Properties:
| 304L Stainless Steel Pipe Density (lb / cu. in.) | 0.29 |
| Specific Gravity(g/cm³) | 7.93 |
| Specific Heat (Btu/lb/Deg°F – [32-212 Deg °F]) | 0.12 |
| Electrical Resistivity (microhm-cm (at 68 Deg °F)) | 432 |
| Melting Point (Deg°F) | 2650 |
| Modulus of Elasticity Tension | 28 |